High Performance and flexibility.
Anti-corrosion material.
Suitable for a large range of finishing.
Available thickness (mm): 0,15 – 0,20 – 0,30 – 0,35 – 0,40 – 0,50.
We have the following cable crimped wire range: 6×0,23 – 12×0,23 – (3×0,20)+(6×0,35).
Traction resistance 230-250Kgs/mm2.
Carbon content 0,75%.
Non- sparking wires.
Suitable for soft finishing in non-ferrous materials.
Traction resistance 80-95 Kgs/mm2.
Available thickness (mm.): 0,08 – 0,30 – 0,40.
High Performance brushes are made of cable wire, made of a bunch of high strength brass coated steel wires, which form a flexible and compact unit. You get a type of finishing and extraction capacity similar to monofilament of 0.30 mm.
They provide important advantages:
The laminated wire is a novelty in the metal brushware industry and it provides an element of comfort and security to the handling of wire brushes. The coating of the wires prevents from being wounded too.
It provides a high performance as a result of the reduced level of breakings of the laminated wires compared to an equivalent wire uncoated.
Suitable for twist-knotted brushes and a high removal capacity. Non suitable for stainless steel surfaces.
Traction resistance 200-275 Kgs/mm2.
Carbon content 0,50-0,60%.
Available thickness (mm): 0,12 – 0,20 – 0,30 – 0,37 – 0,50 – 0,80.
We have 0,10 mm Bessemer wire.
These wires are used for the brushing of stainless steel, aluminium or non ferrous metal surfaces. Stainless steel turned into wire becomes lightly magnetic.
Traction resistance 160-180 Kgs/mm2 following AISI 304-L regulations.
Available thickness (mm): 0,15 – 0,20 – 0,30 – 0,40 – 0,50.
We have stainless steel wire following AISI 316-L regulations and stainless steel cable 7×0,35.
Suitable for soft polishing in silver colour surfaces.
Copper content 60-65%, Zinc 22-25% and Nickel 11-13%.
Available thickness: 0,08 mm
| SYNTHETIC FIBERS | TEMP. RESISTANCE INºC | LIQUID ABSORPTION | 1. GASOLINE | 2. VEGETABLE OIL | 3. BENZOL | 4. TRICHLOROETHYLENE | 5. ACETONE | 6. VASELINE | 7. CAUSTIC SODA | 8. CAUSTIC POTASE | 9. CITRIC ACID | 10. SULFURIC ACID | 11. NITRIC ACID | 12. HYDROCHLORIC ACID | 13. ETHYL ACETATE | PROPERTIES | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Polyamide 6-40 | PA 6-40 | -40 +80 | 10 % | Specifically for low temperatures | |||||||||||||
| Polyamide 6 FH | PA6FH | -20 +100 | 9,5 % | Fiber with a flame retardant | |||||||||||||
| Polyamide 6.6 | PA66 | -30 +110 | 8,5 % | High mechanical resitance to fatigue and to wear | |||||||||||||
| Polyamide 6.12 | PA612 | -30 +110 | 3 % | High quality fibers with excellent shape memory and recovery qualities | |||||||||||||
| Polyamide 6.12 Abrasive | CASI OXAL | -20 +110 | 3 % | High quality abrasive fibers silicon carbide (CASI).Aluminium oxide (OXAL) | |||||||||||||
| Rilsan | RSS | -20 +150 | 3 % | Very high quality for intense tasks | |||||||||||||
| Pekalon | PPS | -30 +190 | 0,02 % | Special for high temperatures | |||||||||||||
| PBT Polyester | PBT | -20 +140 | 0 % | Very high resistance to wear. Food industry | |||||||||||||
| Polypropylene | PP | -15 +80 | 0,6 % | With anti-UV treatment. Good stiffness | |||||||||||||
| Polyethylene | PE | -15 +65 | 0,2 % | Very flexible, high resitance to impact | |||||||||||||
Consult us if you want to have more information related to our services or you want us to advise you about how they can fit to your firm´s needs.
T. +34 943 120 600
info@jazsurface.com
Polígono Ind. Azitain, 4
20600 Eibar – Spain
T. 877.529.8721
59 Tarkiln Place
New Bedford, MA
02745 – USA
We support the Sustainable Development Goals